Superabsorbent crosslinked ampholytic ion pair copolymers

ABSTRACT

The present invention provides crosslinked ampholytic ion pair (2-methacryloyloxyethyldiethylammonium cation (MEDEA)/sulfonate anion) copolymers that are highly absorbent to aqueous electrolyte solutions. The polymers of the present invention comprise polymers formed by the copolymerization of an effective amount of each of the following components to produce a polymer which is highly absorbent to aqueous electrolyte solutions: 
     (a) an ampholytic ion pair monomer comprising 
     (i) the ammonium cation 2-methacryloyloxyethyldiethylammonium and 
     (ii) a sulfonate anion selected from the group consisting of 2-acrylamido-2-methylpropane sulfonate, 2-methacryloyloxyethane sulfonate, vinyl sulfonate, styrene sulfonate and combinations of two or more thereof; 
     (b) at least one comonomer selected from the group consisting of acrylamide, methacrylamide, acylonitrile, acrylic acid, methacrylic acid, alkali salts of acrylic acid, alkali salts of methacrylic acid, 2-methacryloyloxyethyldiethylamine, 2-acrylamido-2-methylpropane sulfonic acid, alkali salts of 2-acrylamido-2-methylpropane sulfonic acid, 2-methacryloyloxyethane sulfonic acid, alkali salts of 2-methacryloyloxyethane sulfonic acid, N-vinyl-2-pyrrolidone and combinations of two or more thereof; and 
     (c) at least one crosslinking agent which has at least two polymerizable olefinic functionalities wherein the olefinic functionalities are suitable for crosslinking. 
     The invention also provides a method of using the polymers of the present invention for absorbing an aqueous electrolyte solution comprising the step of contacting the polymers of the present invention with an aqueous electrolyte solution.

Background of the Invention

1. Field of the Invention

This invention pertains to crosslinked superabsorbent copolymers formed from an ampholytic ion pair (2-methacryloyloxyethyldiethylammonium cation (MEDEA)/sulfonate anion) copolymerized with other comonomers. A further aspect of the invention relates to a method of using the aforesaid crosslinked superabsorbent copolymers for absorbing aqueous electrolyte solutions.

2. Description of the Prior Art

Polymers for absorbing aqueous electrolyte solutions are used in numerous commercial and industrial applications. For example, polymers are used to improve the water absorbency of paper towels and disposable diapers.

Though known water absorbing polymers are highly absorbent to deionized water, they are dramatically less absorbent to aqueous electrolyte solutions such as salt water, brine, and urine. For example, hydrolyzed crosslinked polyacrylamide absorbs 1,024 grams of deionized water per gram of polymer, but only 25 grams of synthetic urine per gram of polymer. Crosslinked polyacrylate absorbs 423 grams of deionized water per gram of polymer, but only 10 grams of synthetic urine per gram of polymer. Hydrolyzed crosslinked polyacrylonitrile absorbs 352 grams of deionized water per gram of polymer, but only 25 grams of synthetic urine per gram of polymer.

It would be a valuable contribution to the art to develop polymers with high absorbency to aqueous electrolyte solutions such as tap water, salt water, brine, and urine. It also would be a valuable contribution to the art to develop inexpensive polymers with high absorbency to aqueous electrolyte solutions. The market for these types of polymers is large and the uses are numerous. Therefore, seemingly small improvements in the absorbency translate into large savings in the quantity of polymer required to absorb these aqueous electrolyte solutions and large savings to the consumer.

SUMMARY OF THE INVENTION

The polymers of the present invention comprise crosslinked polymers formed by the copolymerization of an effective amount of each of the following components to produce a highly absorbent polymer:

(a) an ampholytic ion pair monomer comprising

(i) the ammonium cation 2-methacryloyloxyethyldiethylammonium and

(ii) a sulfonate anion selected from the group consisting of 2-acrylamido-2-methylpropane sulfonate, 2-methacryloyloxyethane sulfonate, vinyl sulfonate, styrene sulfonate and combinations of two or more thereof;

(b) at least one comonomer selected from the group consisting of acrylamide, methacrylamide, acrylonitrile, acrylic acid, methacrylic acid, alkali salts of acrylic acid, alkali salts of methacrylic acid, 2-methacryloyloxyethyldiethylamine, 2-acrylamido-2-methylpropane sulfonic acid, alkali salts of 2-acrylamido-2-methylpropane sulfonic acid, 2-methacryloyloxyethane sulfonic acid, alkali salts of 2-methacryloyloxyethane sulfonic acid, N-vinyl-2-pyrrolidone and combination of two or more thereof; and

(c) at least one crosslinking agent which has at least two polymerizable olefinic functionalities wherein each of the olefinic functionalities are suitable for crosslinking.

A further aspect of the invention relates to a method of absorbing an aqueous electrolyte solution comprising the step of contacting the polymers of the present invention with an aqueous electrolyte solution.

Thus, it is a general object of the present invention to provide the polymers of the present invention having improved absorbency to aqueous electrolyte solutions.

A further object of the present invention is to provide a method of using the polymers of the present invention for absorbing aqueous electrolyte solutions comprising the step of contacting the polymers of the present invention with the aqueous electrolyte solution.

Further objects, features, and advantages of the present invention will be readily apparent to those skilled in the art upon reading the description of the invention which follows.

DESCRIPTION OF THE INVENTION

The present invention provides polymers that are highly absorbent to aqueous electrolyte solutions. Typical aqueous electrolyte solutions include but are not limited to the group consisting of tap water, salt water, brine, and urine. The polymers of the present invention comprise polymers formed by the copolymerization of an effective amount of each of the following components to produce a polymer which is highly absorbent to aqueous electrolyte solutions:

(a) an ampholytic ion pair monomer comprising

(i) an ammonium cation 2-methacryloyloxyethyldiethylammonium (also referred to as MEDEA) and

(ii) a sulfonate anion selected from the group consisting of 2-acrylamido-2-methylpropane sulfonate (also referred to as AMPS® a trademark of Lubrizol for 2-acrylamido-2-methylpropane sulfonic acid), 2-methacryloyloxyethane sulfonate (also referred to as MES), vinyl sulfonate, styrene sulfonate and combinations of two or more thereof;

(b) at least one comonomer selected from the group consisting of acrylamide (also referred to as AM), methacrylamide, acrylonitrile (also referred to as AN), acrylic acid (also referred to as AA), methacrylic acid, alkali salts of acrylic acid (also referred to as X-AA), alkali salts of methacrylic acid, 2-methacryloyloxyethyldiethylamine, 2-acrylamido-2-methylpropane sulfonic acid, alkali salts of 2-acrylamido-2-methylpropane sulfonic acid, 2-methacryloyloxyethane sulfonic acid, alkali salts of 2-methacryloyloxyethane sulfonic acid, N-vinyl-2-pyrrolidone and combinations of two or more thereof; and

(c) at least one crosslinking agent which has at least two polymerizable olefinic functionalities wherein each of the olefinic functionalities are suitable for crosslinking.

As used in this application, the term "alkali salts" is used generically, unless otherwise indicated, to mean alkali salts including but not limited to salts containing lithium, sodium, potassium, and ammonium cations.

As used in this application, the term "monomer" is used generically, unless otherwise indicated, to mean monomers, comonomers, termonomers, tetramonomers, etc. The term "comonomer" is used generically, unless otherwise indicated, to mean monomers, comonomers, termonomers, tetramonomers, etc. for polymers wherein there are at least two different monomers.

As used in this application, the term "polymer" is used generically, unless otherwise indicated, to mean homopolymers, copolymers, terpolymers, tetrapolymers, etc., and thus includes polymers prepared using any number of monomers. The term "copolymer" is used generically, unless otherwise indicated, to mean polymers prepared using two or more different monomers.

As used in this application, the term "hydrolysis" is used generically, unless otherwise indicated, to include hydrolysis of nitrile functionalities and hydrolysis of amide functionalities. These hydrolysis reactions are loosely referred to in the art as "saponification." Hydrolysis of these functionalities may occur under acidic or basic conditions. Under basic hydrolysis conditions, the term may also include, unless otherwise indicated, neutralization of carboxylic acid and sulfonic acid functinalities.

The ampholytic ion pair monomer used in the present invention may be prepared by titrating an aqueous solution of a sulfonic acid monomer to pH 7 with 2-methacryloyloxyethyldiethylamine at a temperature of about 0°-15° C. The resulting aqueous solution containing the ampholytic ion pair may be purified by contacting the aqueous solution one or more times with small quantities of activated charcoal. The concentration of the ampholytic ion pair in the aqueous solution may be determined by evaporatively drying a known amount of the aqueous solution and weighting the residue.

Alternatively, the ampholytic ion pair monomer for use in the preparation of the present invention may be prepared by methods which are well known to those skilled in the art. For example, one of the ampholytic ion pair monomers can be prepared by reacting 2-methacryloyloxyethyldiethylamine with commercially available 2-acrylamido-2-methylpropane sulfonic acid or 2-methacryloyloxyethane sulfonic acid in anhydrous tetrahydrofuran. See J. C. Salamone, C. C. Tsai, A. P. Olson, and A. C. Watterson, Adv. Chemical Series, Volume 187, pages 337-346.

The olefinic comonomers can include but are not limited to the group consisting of acrylamide, methacrylamide, acrylonitrile, acrylic acid, methacrylic acid, alkali salts of acrylic acid, alkali salts of methacrylic acid, 2-methacryloyloxyethyldiethylamine, 2-acrylamido-2-methylpropane sulfonic acid, alkali salts of 2-acrylamido-2-methylpropane sulfonic acid, 2-methacryloyloxyethane sulfonic acid, alkali salts of 2-methacryloyloxyethane sulfonic acid, N-vinyl-2-pyrrolidone and combinations of two or more thereof. Most of these olefinic comonomers are believed to be commercially available.

Suitable crosslinking agents can include but are not limited to the group consisting of N,N-diallylmethacrylamide, diallylamine, N,N-bisacrylamidoacetic acid, N,N'-bisacrylamidoacetic acid methylester, N,N'-methylenebisacrylamide (methylene-bis-acrylamide), N,N-benzylidenebisacrylamide, allylacrylate, diisopropenylbenzene, diallyl succinate, ethylene glycol diacrylate, diallylacrylamide, divinylbenzene, and combinations of two or more thereof. All the listed crosslinking agents are believed to be commercially available.

The polymers of the present invention were generally prepared by mixing the various monomers in the desired stoichiometric ratios in aqueous solution and then initiating the free-radical copolymerization. The copolymerization of the ampholytic ion pair monomer with the olefinic comonomer and crosslinking agent can be achieved by any of the well known free-radical polymerization techniques in solution, suspension, or emulsion environment. Well known azo compounds commonly employed to initiate free radical polymerization reactions include 2,2'-azobis(N,N'-dimethylisobutyramidine)dihydrochloride, azobisisobutyronitrile, 4,4'-azobis(4-cyanovaleric acid), 2,2'-azobis(2,4-dimethyl(4-methyoxyvaleronitrile), 2,2'-azobis(2,4-dimethylvaleronitrile), 2,2'-azobis(2-amidinopropane)dihydrochloride, 2-t-butylazo-2-cyano-4-methoxy-4-methylpentane, and 2-t-butylazo-2-cyano-4-methylpentane, and 4-t-butylazo-4-cyanovaleric acid. Well known inorganic peroxide compounds commonly employed to initiate free radical polymerization reactions include hydrogen peroxide, alkali metal persulfates, alkali metal perborates, alkali metal perphosphates, and alkali metal percarbonates. Well known organic peroxide compounds commonly employed to initiate free radical polymerization reactions include lauryl peroxide, 2,5-dimethyl-2,5-bis(ethylhexanoylperoxy)hexane, t-butylperoxypivilate, t-butylperoctoate, p-menthane hydroperoxide, and benzoylperoxide. The compound t-butylhyponitrite is a well known alkyl hyponitrite commonly employed to initiate free radical polymerization reactions. Furthermore, ultraviolet light is commonly employed to initiate free radical polymerization reactions. In addition, such other methods of copolymerization as would have occurred to one skilled in the art may be employed, and the present invention is not limited to the particular method of preparing the crosslinked polymer set out herein.

These inventive copolymers containing an olefinic comonomer with amide, nitrile, carboxylic acid, or sulfonic acid functionalities or crosslinking agent with amide, nitrile, carboxylic acid, or sulfonic acid functionalities can optionally be at least partially hydrolyzed and/or neutralized by heating with aqueous base such as aqueous sodium hydroxide or aqueous potassium hydroxide. The degree of hydrolysis and/or neutralization can be controlled by stoichiometrically limiting the amount of base relative to the amount of amide, nitrile, carboxylic acid, and sulfonic acid functionalities. If the hydrolysis is carried out under acidic conditions, the amide and nitrile functionalities can be converted to carboxylic acid functionalities without neutralizing the carboxylic acid or sulfonic acid functionalities of the polymer.

The broadest range for the compositions of the inventive crosslinked MEDEA/sulfonate copolymers is an effective amount of each of the ampholytic ion pair monomer, olefinic comonomer, and crosslinking agent to produce a polymer highly absorbent to aqueous electrolyte solutions.

The preferred ranges for the compositions of the inventive polymers given in Tables I, II, and III reflect the relative stoichiometric amount in mole percent based on the total number of moles of all the various monomers mixed together before the copolymerization. The ratio of the crosslinking agent to the other monomers is based on the total number of moles of the ampholytic ion pair and the comonomers. The actual composition of the polymers of the present invention produced by the copolymerization reaction may vary slightly from the stoichiometric mixture before the copolymerization depending on the the reaction conditions.

The broad and preferred ranges for the compositions of the inventive crosslinked MEDEA/sulfonate copolymers are given in Table I. The broad ranges for the compositions of the present invention are based on the experimental data provided in Example V, Tables VIII and IX, for those polymer compositions which produce an absorbency of at least 70 gram of synthetic urine per gram of inventive crosslinked MEDEA/sulfonate copolymer.

                  TABLE I                                                          ______________________________________                                         Broad And Preferred Ranges Of Compositions For Inventive                       Polymers                                                                       MEDEA/                                  LINK                                   sulfonate    AM      AN      AA   X-AA  mole                                   MOLE PERCENT                ratio*                                             ______________________________________                                         broad  3-50      50-97   --    --   --    0.01-0.3                             preferred                                                                             3-30      70-97   --    --   --    0.03-0.2                             broad  3-30      --      70-97 --   --    0.01-0.3                             preferred                                                                             5-25      --      75-95 --   --    0.03-0.2                             broad  3-6       --      --    --   94-97 0.01-0.3                             preferred                                                                             3         --      --    --   97    0.03-0.2                             broad  1-55      10-55   --    --   32-89 0.01-0.3                             preferred                                                                             3-50      13-50   --    --   37-84 0.03-0.2                             ______________________________________                                          MEDEA/sulfonate = 2methacryloyloxyethyldiethylammonium cation/a sulfonate      anion selected from the group consisting of 2acrylamido-2-methylpropane        sulfonate, 2methacryloyloxyethane sulfonate, and any combination thereof       AM = Acrylamide                                                                AN = Acrylonitrile                                                             AA = Acrylic Acid                                                              X-AA = Alkali Salt of Acrylic Acid (Acrylate)                                  LINK = CrossLinking Agent                                                      *mole ratio = mole crosslinking agent per 100 mole of the ampholytic ion       pair monomer and the comonomers.                                         

The more preferred and most preferred ranges for the compositions of the inventive crosslinked MEDEA/AMPS copolymers are given in Table II. These more preferred and most preferred ranges for the compositions of the present invention are based on the experimental data provided in Example V, Table VIII, for those polymer compositions which produce an absorbency of at least 70 gram of synthetic urine per gram of inventive MEDEA/AMPS polymer.

                                      TABLE II                                     __________________________________________________________________________     Preferred Compositions For Inventive MEDEA/AMPS Polymers                               MEDEA/AMPS                                                                              AM  AN  AA X-AA                                                                               LINK                                                   MOLE PERCENT            mole ratio*                                    __________________________________________________________________________     more preferred                                                                         3-30     70-97                                                                              --  -- --  0.01-0.2                                       most preferred                                                                         5-20     80-95                                                                              --  -- --  0.03-0.2                                       more Preferred                                                                         3-25     --  75-97                                                                              -- --  0.01-0.2                                       most preferred                                                                         5-20     --  80-95                                                                              -- --  0.03-0.2                                       more preferred                                                                         3-6      --  --  -- 94-97                                                                              0.01-0.2                                       most preferred                                                                         3        --  --  -- 97  0.03-0.2                                       more preferred                                                                         3-15     15-30                                                                              --  -- 55-82                                                                              0.01-0.2                                       most preferred                                                                         3-10     20-25                                                                              --  -- 70-77                                                                              0.03-0.2                                       __________________________________________________________________________      MEDEA/AMPS = 2methacryloyloxyethyldiethylammonium                              cation/2acrylamido-2-methylpropane sulfonate                                   AM = Acrylamide                                                                AN = Acrylonitrile                                                             AA = Acrylic Acid                                                              X-AA = Alkali Salt of Acrylic Acid (Acrylate)                                  LINK = CrossLinking Agent                                                      *mole ratio = mole crosslinking agent per 100 mole of the ampholytic ion       pair monomer and the comonomers.                                         

The more preferred and most preferred ranges for the compositions of the inventive crosslinked MEDEA/MES copolymers are given in Table III. These more preferred and most preferred ranges for the compositions of the present invention are based on the experimental data provided in Example V, Table IX, for those polymer compositions which produce an absorbency of at least 70 gram of synthetic urine per gram of inventive crosslinked MEDEA/MES copolymer.

                                      TABLE III                                    __________________________________________________________________________     Preferred Compositions For Inventive MEDEA/MES Polymers                                MEDEA/MES                                                                              AM  AN  AA X-AA                                                                               LINK                                                    MOLE PERCENT           mole ratio*                                     __________________________________________________________________________     more preferred                                                                         3-50    50-97                                                                              --  -- --  0.01-0.2                                        most preferred                                                                         3-30    70-97                                                                              --  -- --  0.03-0.2                                        more preferred                                                                         3-30    --  70-97                                                                              -- --  0.01-0.2                                        most preferred                                                                         6-25    --  75-94                                                                              -- --  0.03-0.2                                        more preferred                                                                         3-6     --  --  -- 94-97                                                                              0.01-0.2                                        most preferred                                                                         3       --  --  -- 97  0.03-0.2                                        more preferred                                                                         1-55    10-55                                                                              --  -- 32-89                                                                              0.01-0.2                                        most preferred                                                                         3-50    13-50                                                                              --  -- 37-84                                                                              0.03-0.2                                        __________________________________________________________________________      MEDEA/MES = 2methacryloyloxyethyldiethylammonium                               cation/2methacryloyloxyethane sulfonate                                        AM = Acrylamide                                                                AN = Acrylonitrile                                                             AA = Acrylic Acid                                                              X-AA = Alkali Salt of Acrylic Acid (Acrylate)                                  LINK = CrossLinking Agent                                                      *mole ratio = mole crosslinking agent per 100 mole of the ampholytic ion       pair monomer and the comonomers.                                         

A further aspect of the invention relates to a method of absorbing aqueous electrolyte solutions comprising the step of contacting the polymers of the present invention with the aqueous solution. Typical aqueous electrolyte solutions are not limited to but may be selected from the group consisting of tap water, salt water, brine, and urine. For the purposes of this specification tap water is defined to have an electrolyte concentration of less than 500 ppm of dissolved electroytes, urine is defined to have an electrolyte concentration of from greater than 500 ppm to at most 10,000 ppm dissolved elecrolytes, salt water is defined to have an electrolyte concentration from greater than 10,000 ppm to at most 34,000 ppm and brine is defined to have an electrolyte concentration of greater than 34,000 ppm to the saturation point of the aqueous solution.

The following examples are intended to illustrate the advantages of this invention but are not intended to unduly limit this invention.

EXAMPLE I

The control data in Table IV demonstrates that although known polymers are highly absorbent to deionized water, they are dramatically less absorbent to aqueous electrolyte solutions such as salt water and urine. Known polymer compositions include crosslinked polyacrylamide, partially saponified crosslinked polyacrylamide, crosslinked polyacrylonitrile, partially saponified crosslinked acrylonitrile, crosslinked polyacrylic acid, neutralized crosslinked polyacrylic acid, crosslinked polyacrylate, and polymers thereof with sodium 2-acrylamido-2-methylpropane sulfonate. The best of these known polymers absorbs up to about 60 grams of urine per gram of polymer, and most of the known polymers absorb much less than 50 grams of urine per gram of polymer.

The polymers of the control data were prepared by mixing the monomers in the proportions given in Table IV in an aqueous solution of deionized water. The monomers were present in about 30-40 weight percent relative to the amount of deionized water. The free radical polymerization was initiated with commercially available 2,2'-azobis(N,N'-dimethylisobutyramidine) dihydrochloride. About 0.1 mole percent based on the total moles of the monomers of the azo free-radical inditiator was employed. The reaction mixture was then degassed by bubbling nitogen gas through the mixture for 15 minutes. The reaction temperature was maintained between 20°-35° C. for 24 hours. The reactions produced transparent or cloudy hard gels of the crosslinked polymers. A large volume of deionized water was added to the polymer product and the polymers were allowed to swell for about 24 hours. The swelled polymers were dried in a forced convection oven at 74° C. The dried polymers were then mechanically blended to a powder.

Some of the polymers were hydrolyzed and neutralized with a strong base such as aqueous sodium hydroxide or aqueous potassium hydroxide. The degree of hydrolysis or neutralization could be controlled by stoichiometrically limiting the amount of base relative to the amount of amide, nitrile, or carboxylic acid functionalities. A suspension of 1 gram of the polymer in about 20 milliliters of 0.5 molar aqueous sodium hydroxide was heated to 95° C. until a light golden-yellow color was obtained. The mixture was then transferred to a dialysis bag with a molecular weight cut-off of 12,000-14,000 and dialyzed exhaustively against distilled water until the viscous polymer gel had reached pH 7. This viscous polymer gel was then poured into a plastic dish and dried in a forced convection oven at 74° C. The dried polymers were then mechanically blended to a powder.

The dried polymers were then tested for deionized water absorption and synthetic urine absorption. About 1 liter of deionized water or synthetic urine was added to 0.1 to 0.5 gram of the dried polymer and allowed to stand for 24 hours. The polymer was then separated from the excess unabsorbed liquid by screening through a 100 mesh per inch stainless steel sieve. The absorbency was determined by weighing the isolated polymer containing the absorbed liquid and subtracting the weight of the dry polymer. The absorbency was measured in units of grams of liquid per grams of polymer. The synthetic urine was prepared by dissolving 0.64 gram CaCl₂, 1.14 gram MgSO₄.7H₂ O, 8.20 gram NaCl, and 20.0 gram urea into 1000 gram deionized water. Several of the polymers were tested two or three times, and the experimental error was within plus or minus 2-5 percent. This small experimental error was largely caused by gel blocking and minor diffusion problems that prevented the aqueous liquid from contacting with all the polymer.

                                      TABLE IV                                     __________________________________________________________________________     Control Data                                                                   AMPS    AM AN AA X-AA LINK      DIW SU                                         EXP#                                                                               MOLE PERCENT      mole ratio*                                                                          XOH g/g**                                          __________________________________________________________________________     126A                                                                               --  100                                                                               -- -- --   0.05  NO   17 15                                         126 --  100                                                                               -- -- --   0.05  YES 1024                                                                               25                                         406R                                                                               --  100                                                                               -- -- --   0.05  YES 364 40                                         125A                                                                               --  100                                                                               -- -- --   0.20  NO   13   12.5                                     125 --  100                                                                               -- -- --   0.20  YES 295 16                                          26 --  -- 100                                                                               -- --   0.05  YES 608 46                                         405 --  -- 100                                                                               -- --   0.10  NO   0   0                                         405 --  -- 100                                                                               -- --   0.10  YES 414 42                                         129 --  -- 100                                                                               -- --   0.20  YES 352 25                                         127A                                                                               --  -- -- 100                                                                               --   0.20  NO   21 11                                         127 --  -- -- 100                                                                               --   0.20  Neutr.                                                                             423 10                                         194 --  -- -- -- 100 (K)                                                                             0.05  NO  669 57                                         204 --  -- -- -- 100 (Na)                                                                            0.05  NO  505 41                                         211 --  13 -- -- 87   0.05  NO  --  65                                         267 3   13 -- -- 84   0.05  NO  350 38                                         372 3   20 -- -- 77   0.05  NO  417 47                                          20 6   13 -- -- 81   0.05  NO  738 56                                          21 6   26 -- -- 68   0.05  NO  533 47                                          22 6   -- -- -- 94   0.05  NO  488 55                                          23 10  13 -- -- 77   0.05  NO  570 59                                          25 20  13 -- -- 67   0.05  NO  624 62                                          19 100 -- -- -- --   0.05  NO  Soluble                                        __________________________________________________________________________      AMPS = 2acrylamido-2-methylpropane sulfonic acid (Note: AMPS is a              trademark of Lubrizol Corporation)                                             AM = Acrylamide                                                                AN = Acrylonitrile                                                             AA = Acrylic Acid                                                              X-AA = Alkali Salt of Acrylic Acid (Acrylate)                                  LINK = Methylenebis-acrylamide CrossLinking Agent                              *mole ratio = mole crosslinking agent per 100 mole of the ampholytic ion       pair monomer and the comonomers.                                               XOH = Basic Hydrolysis and/or Neutralization with aqueous NaOH or KOH          DIW = Deionized Water                                                          SU = Synthetic Urine                                                           **g/g = absorbency units of gram aqueous liquid per gram dried polymer   

EXAMPLE II

The control data in Table V demonstrates that although commercially available water absorbing materials are highly absorbent to water, they are also dramatically less absorbent to aqueous electrolyte solutions such as salt water and urine. The commercially available water absorbing materials tested include poly(co-acrylamide-co-acrylic acid) grafted onto starch, a commercial acrylamide polymer sold under the trademark "Water Grabber"® ("Water Grabber" is a trademark of F. P. Products, Inc.), "LUVS"® diaper absorbent ("LUVS" is a trademark of Proctor & Gamble Co.), "Pampers"® diaper absorbent ("Pampers" is a trademark of Proctor & Gamble Co.), and "Favor 960"® (Stockhausen, Inc.). The best of these known materials absorb up to about 56 grams of urine per gram of absorbing material, and most of the known polymers absorb much less than 40 grams of urine per gram of absorbing material.

                  TABLE V                                                          ______________________________________                                         Control Data For Commercial Materials                                                                   DIW  SU                                               EXP#  Commercial Material      g/g*                                            ______________________________________                                         1     COMMERCIAL STARCH-g-POLY 345    37                                             (AM-AA)                                                                  2     WATER GRABBER  ® (AM 440    34                                             COPOLYMER)                                                               3     LUVS  ® DIAPER ABSORBENT                                                                            191    16                                       4     PAMPERS  ® DIAPER ABSORBENT                                                                         171    12                                       5     FAVOR 960  ®         369    56                                       ______________________________________                                          g = graft                                                                      AM = Acrylamide                                                                AA = Acrylic Acid                                                              DIW = Deionized Water                                                          SU = Synthetic Urine                                                           *g/g = absorbency units of gram aqueous liquid per gram dried polymer    

EXAMPLE III

The homopolymers of the ampholytic ion pair monomers comprising 2-methacryloyloxyethyldiethylammonium 2-acrylamido-2-methylpropane sulfonate (MEDEA/AMPS) ("AMPS" is a trademark of Lubrizol Corporation for 2-acrylamido-2-methylpropane sulfonic acid) or 2-methacryloyloxyethyldiethylammonium 2-methacryloyloxyethane sulfonate (MEDEA/MES) with 0.05 weight percent methylene-bis-acrylamide cross linking agent was tested for these absorbency to deionized water and synthetic urine. The absorbency of homopolymers is very poor. See Table VI. The absorbency to deionized water is less than 10 gram water per gram of homopolymer, and only 10 and 29 gram synthetic urine per gram of homopolymer, respectively.

                  TABLE VI                                                         ______________________________________                                         Control Data For Ion Pair Homopolymer                                          MEDEA/      MEDEA/                                                             AMPS        MES       LINK         DIW  SU                                     EXP#  MOLE PERCENT    MOLE RATIO*  g/g**                                       ______________________________________                                         21    100       --        0.05       4.6   8                                    5    100       --        0.06       7    10                                   36    --        100       0.05       13   29                                   ______________________________________                                          MEDEA/AMPS = 2methacryloyloxyethyldiethylammonium cation                       2acrylamido-2-methylpropane sulfonate anion                                    MEDEA/MES = 2methacryloyloxyethyldiethylammonium cation                        2methacryloyloxyethane sulfonate anion                                         LINK = Methylenebis-acrylamide CrossLinking Agent                              DIW = Deionized Water                                                          SU = Synthetic Urine                                                           *Mole Ratio is the moles of crosslinking agent per 100 moles of the ion        pair plus the moles of any comonomers.                                         **g/g = absorbency units of gram aqueous liquid per gram dried polymer   

EXAMPLE IV

The control data in Table VII demonstrates that although the known ampholytic ion pair 3-methacrylamidopropyltrimethylammonium 2-acrylamido-2-methylpropane sulfonate (MPTMA/AMPS) copolymerized with acrylamide is highly absorbent to deionized water, it is dramatically less absorbent to aqueous electrolyte solutions such as salt water, brine, and urine. The absorbency to synthetic urine is about the same as for the better of the known polymers and commercial materials. The MPTMA/AMPS-acrylamide copolymer also has been grafted onto starch using ceric ion or cobalt-60 irradiation. These starch grafted copolymers are poorly absorbent to deionized water, and only slightly more absorbent to synthetic urine. The better of these known polymers absorbs up to about 56 grams of urine per gram of polymer, but the rest absorb less than 30 grams of urine per gram of polymer.

                                      TABLE VII                                    __________________________________________________________________________     Control Data For Known MPTMA/AMPS-Acrylamide Copolymers                        MPTMA/AMPS   AM Starch                                                                             LINK      DIW SU                                           EXP#                                                                               MOLE PERCENT    mole ratio*                                                                          XOH g/g**                                            __________________________________________________________________________         10       90 --  --    NO  soluble                                          87  10       90     0.20  YES 428 56                                           *** 8.56     27.30                                                                             64.86                                                                              --    NO  9.83                                                                               16.21                                        *** 8.98     41.76                                                                             49.26                                                                              --    NO  11.54                                                                              16.62                                        *** 15.01    64.96                                                                             20.03                                                                              --    NO  14.11                                                                              29.45                                        __________________________________________________________________________      MPTMA/AMPS = 3methacrylamidopropyltrimethylammonium                            cation/2acrylamido-2-methylpropane sulfonate anion                             AM = Acrylamide                                                                LINK = Methylenebis-acrylamide CrossLinking Agent                              XOH = Basic Hydrolysis and/or Neutralization with aqueous NaOH or KOH          DIW = Deionized Water                                                          SU = Synthetic Urine                                                           *mole ratio = mole crosslinking agent per 100 mole of the ampholytic ion       pair monomer and the comonomers.                                               **g/g = absorbency units of gram aqueous liquid per gram dried polymer         ***J. C. Salamone, E. L. Rodriguez, K. C. Lin, L. Quach, A. C. Watterson       and I. Ahmed, Polymer 26, 1234-38 (1985).                                

EXAMPLE V

The polymers of the present invention were prepared according to the method described in Example I, except that the inventive polymers were prepared by mixing the monomers in the proportions given in Tables VIII and IX.

The inventive polymers were tested for absorbency to deionized water and synthetic urine. The tested polymers of the present invention comprise polymers formed by the copolymerization with the amount of each of the components set forth in the following tables.

Some of these inventive polymers in this example which contain an olefinic comonomer with amide, nitrile, carboxylic acid, or sulfonic acid functionalities or crosslinking agent with amide, nitrile, carboxylic acid, or sulfonic acid functionalities were hydrolyzed and neutralized with an aqueous base such as aqueous sodium hydroxide or aqueous potassium hydroxide.

                                      TABLE VIII                                   __________________________________________________________________________     Experimental Data For Inventive MEDEA/AMPS Polymers                            MEDEA/AMPS   AM AN AA X-AA                                                                               LINK      DIW                                                                               SU                                      EXP#                                                                               MOLE PERCENT          mole ratio*                                                                          XOH g/g**                                      __________________________________________________________________________     22   5       95 -- -- --  0.05  YES 750                                                                               102                                     23  10       90 -- -- --  0.05  YES 750                                                                                91                                     24  15       85 -- -- --  0.05  YES 669                                                                               109                                     25  20       80 -- -- --  0.05  YES 630                                                                               116                                      6   5       -- 95 -- --  0.06  YES 507                                                                                81                                      7  10       -- 90 -- --  0.06  YES 512                                                                                93                                      8  15       -- 85 -- --  0.06  YES 520                                                                                99                                      9  20       -- 80 -- --  0.06  YES 567                                                                               106                                     26   3       20 -- -- 77  0.05  NO  751                                                                               100                                     27   5       20 -- -- 75  0.05  NO  780                                                                               109                                     28  10       20 -- -- 70  0.05  NO  744                                                                               118                                     __________________________________________________________________________      MEDEA/AMPS = 2methacryloyloxyethyldiethylammonium                              cation/2acrylamido-2-methylpropane sulfonate anion                             AM = Acrylamide                                                                AN = Acrylonitrile                                                             AA = Acrylic Acid                                                              X-AA = Alkali Salt of Acrylic Acid (Acrylate)                                  LINK = Methylenebis-acrylamide CrossLinking Agent                              XOH = Basic Hydrolysis and/or Neutralization with aqueous NaOH or KOH          DIW = Deionized Water                                                          SU = Synthetic Urine                                                           *mole ratio = mole crosslinking agent per 100 mole of the ampholytic ion       pair monomer and the comonomers.                                               **g/g = absorbency units of gram aqueous liquid per gram dried polymer   

                                      TABLE IX                                     __________________________________________________________________________     Experimental Data For Inventive MEDEA/MES Polymers                             MEDEA/MES   AM AN AA X-AA                                                                               LINK      DIW  SU                                     EXP#                                                                               MOLE PERCENT         mole ratio*                                                                          XOH g/g**                                       __________________________________________________________________________     37   6      94 -- -- --  0.05  YES 785  100                                    165 10      90 -- -- --  0.03  YES 1400 113                                    38  10      90 -- -- --  0.05  YES 878  110                                    166 15      85 -- -- --  0.03  YES 1260 87                                     39  15      85 -- -- --  0.05  YES 412  101                                    167 20      80 -- -- --  0.03  YES 966  65                                     40  20      80 -- -- --  0.05  YES 508  111                                    41  25      75 -- -- --  0.05  YES 429  94                                     42  50      50 -- -- --  0.05  YES 389  70                                     43   6      -- 94 -- --  0.05  YES 540  89                                     44  10      -- 90 -- --  0.05  YES 453  110                                    45  15      -- 85 -- --  0.05  YES 502  116                                    46  20      -- 80 -- --  0.05  YES 330  80                                     47  25      -- 75 -- --  0.05  YES 348  75                                     48  50      -- 50 -- --  0.05  YES microgel                                    51   3      -- -- -- 97  0.05  NO  360  70                                     52   3      13 -- -- 84  0.05  NO  629  85                                     57   3      20 -- -- 77  0.05  NO  700  81                                     58   3      35 -- -- 62  0.05  NO  800  79                                     59   3      50 -- -- 47  0.05  NO  757  78                                     53   6      13 -- -- 81  0.05  NO  501  109                                    54  10      13 -- -- 77  0.05  NO  491  91                                     55  20      13 -- -- 67  0.05  NO  500  95                                     56  50      13 -- -- 37  0.05  NO  463  76                                     __________________________________________________________________________      MEDEA/MES = 2methacryloyloxyethyldiethylammonium                               cation/2methacryloyloxyethane sulfonate anion                                  AM = Acrylamide                                                                AN = Acrylonitrile                                                             AA =  Acrylic Acid                                                             X-AA = Alkali Salt of Acrylic Acid (Acrylate)                                  LINK = Methylenebis-acrylamide CrossLinking Agent                              XOH = Basic Hydrolysis and/or Neutralization with aqueous NaOH or KOH          DIW = Deionized Water                                                          SU = Synthetic Urine                                                           *mole ratio = mole crosslinking agent per 100 mole of the ampholytic ion       pair monomer and the comonomers.                                               **g/g = absorbency units of gram aqueous liquid per gram dried polymer   

The data in Tables VIII and XI demonstrates that these polymers exhibit significantly improved absorbency to aqueous electrolyte solutions such as urine over the absorbency of the known polymers listed in Table IV, the commercially available materials listed in Table V, the crosslinked MEDEA/sulfonate homopolymers listed in Table VI, and the analogous crosslinked MPTMA/AMPS-acrylamide copolymers listed in Table VII.

The absorbency of these polymers to urine is highly unexpected in view of the fact that the homopolymers of MEDEA/sulfonate with 0.05 weight percent crosslinking agent only absorb about 10 grams of synthetic urine per gram of the polymer. See Table VI. This demonstrates that the monomers when combined into the polymers of the present invention act synergistically to increase the absorbency of the polymers to aqueous liquids such as salt water and urine.

Taking an absorbency of about 56 grams of synthetic urine per gram of polymer as about the best of the known polymers, the preferred polymers of the present invention exceed this absorbency to urine by 25-107 percent (70-116 grams synthetic urine per gram of inventive polymer, Table VIII and Table IX, compared to 56 grams urine per gram for the best known materials, Tables IV, V, VI, and VII) without sacrificing absorbency to deionized water. These improved absorbencies translate into large savings in the quantity of polymer required and large savings to the consumer.

Reasonable variations can be made in view of the foregoing disclosure without departing from the spirit or scope of the present invention. 

We claim:
 1. A polymer formed by the copolymerization of an effective amount of each of the following components to produce a polymer which will absorb at least 70 grams of synthetic urine per gram of polymer:(a) an ampholytic ion pair monomer comprising(i) the ammonium cation 2-methacryloyloxyethyldiethylammonium and (ii) a sulfonate anion selected from the group consisting of 2-acrylamido-2-methylpropane sulfonate, 2-methacryloyloxyethane sulfonate, vinyl sulfonate, styrene sulfonate, and combinations of two or more thereof; (b) at least one comonomer selected from the group consisting of acrylamide, methacrylamide, acrylonitrile, acrylic acid, methacrylic acid, alkali salts of acrylic acid, alkali salts of methacrylic acid, N-vinyl-2-pyrrolidone and combinations or two or more thereof; and (c) at least one crosslinking agent which has at least two polymerizable olefinic functionalities wherein each of the olefinic functionalities is suitable for crosslinking.
 2. The polymer of claim 1 wherein the crosslinking agent is selected from the group consisting of N,N-diallylmethacrylamide, diallylamine, N,N-bisacrylamidoacetic acid, N,N'-bisacrylamidoacetic acid methylester, N,N'-methylenebisacrylamide (methylene-bis-acrylamide), N,N-benzylidenebisacrylamide, allylacrylate, diisopropenylbenzene, diallyl succinate, ethylene glycol diacrylate, diallylacrylamide, divinylbenzene, and combinations of two or more thereof.
 3. The polymer of claim 2 wherein the crosslinking agent comprises N,N'-methylenebisacrylamide.
 4. The polymer of claim 1 wherein the polymer is at least partially hydrolyzed.
 5. The polymer of claim 1 wherein the polymer is at least partially neutralized.
 6. The polymer of claim 1 wherein the comonomer is selected from the group consisting of acrylamide, acrylonitrile, acrylic acid, alkali salts of acrylic acid, and combinations of two or more thereof.
 7. The polymer of claim 6 wherein the comonomer is acrylamide.
 8. A polymer formed by the copolymerization of an effective amount of each of the following components to produce a polymer which is highly absorbent to aqueous electrolyte solutions:(a) an ampholytic ion pair monomer comprising(i) the ammonium cation 2-methacryloyloxyethyldiethylammonium and (ii) a sulfonate anion selected from the group consisting of 2-acrylamido-2-methylpropane sulfonate, 2-methacryloyloxyethane sulfonate, vinyl sulfonate, styrene sulfonate, and combinations of two or more thereof; (b) a comonomer selected from the group consisting of acrylamide and methacrylamide; (c) at least one crosslinking agent which has at least two polymerizable olefinic functionalities wherein each of the olefinic functionalities is suitable for crosslinking; wherein the polymer is formed by the polymerization of in the range of about 3 mole percent to about 50 mole percent of the ampholytic ion pair monomer, and in the range of about 50 mole percent to about 97 mole percent of the comonomer wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and in the range of of about 0.01 mole of the crosslinking agent to about 0.3 mole of the crosslinking agent per 100 moles of the ampholytic ion pair monomer and the comonomer.
 9. The polymer of claim 8 wherein the polymer is formed by the polymerization of:(a) in the range of about 3 mole percent to about 30 mole percent of the ampholytic ion pair monomer, and (b) in the range of about 70 mole percent to about 97 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.03 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 10. The polymer of claim 8 wherein the sulfonate anion is 2-acrylamido-2-methylpropane sulfonate.
 11. The polymer of claim 10 wherein the polymer is formed by the polymerization of:(a) in the range of about 3 mole percent to about 30 mole percent of the ampholytic ion pair monomer, and (b) in the range of about 70 mole percent to about 97 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.01 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 12. The polymer of claim 11 wherein the polymer is formed by the polymerization of:(a) in the range of about 5 mole percent to about 20 mole percent of the ampholytic ion pair monomer, and (b) in the range of about 80 mole percent to about 95 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.03 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 13. The polymer of claim 8 wherein the sulfonate anion is 2-methacryloyloxyethane sulfonate.
 14. The polymer of claim 13 wherein the polymer is formed by the polymerization of:(a) in the range of about 3 mole percent to about 50 mole percent of the ampholytic ion pair monomer, and (b) in the range of about 50 mole percent to about 97 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.01 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 15. The polymer of claim 14 wherein the polymer is formed by the polymerization of:(a) in the range of about 3 mole percent to about 30 mole percent of the ampholytic ion pair monomer, and (b) in the range of about 70 mole percent to about 97 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.02 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 16. The polymer of claim 6 wherein the comonomer is acrylonitrile.
 17. A polymer formed by the copolymerization of an effective amount of each of the following components to produce a polymer which is highly absorbent to aqueous electrolyte solutions;(a) an ampholytic ion pair monomer comprising(i) the ammonium cation 2-methacryloyloxyethyldiethylammonium and (ii) a sulfonate anion selected from the group consisting of 2-acrylamido-2-methylpropane sulfonate, 2-methacryloyloxyethane sulfonate, vinyl sulfonate, styrene sulfonate, and combinations or two or more thereof; (b) an acrylonitrile comonomer and; (c) at least one crosslinking agent which has at least two polymerizable olefinic functionalities wherein each of the olefinic functionalities is suitable for crosslinking; wherein the polymer is formed by the polymerization of in the range of 3 mole percent to about 30 mole percent of the ampholytic ion pair monomer, and in the range of about 70 mole percent to about 97 mole percent of the acrylonitrile comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and in the range of about 0.01 mole of the crosslinking agent to about 0.3 mole of the crosslinking agent per 100 moles of the ampholytic ion pair monomer and the comonomer.
 18. The polymer of claim 17 wherein the polymer is formed by the polymerization of:(a) in the range of about 5 mole percent to about 25 mole percent of the ampholytic ion pair monomer, and (b) in the range of about 75 mole percent to about 95 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.03 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 19. The polymer of claim 17 wherein the sulfonate anion is 2-acrylamido-2-methylpropane sulfonate.
 20. The polymer of claim 19 wherein the polymer is formed by the polymerization of:(a) in the range of about 3 mole percent to about 25 mole percent of the ampholytic ion pair monomer, and (b) in the range of about 75 mole percent to about 97 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.01 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 21. The polymer of claim 20 wherein the polymer is formed by the polymerization of:(a) in the range of about 5 mole percent to about 20 mole percent of the ampholytic ion pair monomer, and (b) in the range of about 80 mole percent to about 95 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.03 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 22. The polymer of claim 17 wherein the sulfonate anion is 2-methacryloyloxyethane sulfonate.
 23. The polymer of claim 22 wherein the polymer is formed by the polymerization of:(a) in the range of about 3 mole percent to about 30 mole percent of the ampholytic ion pair monomer, and (b) in the range of about 70 mole percent to about 97 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.01 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 24. The polymer of claim 23 wherein the polymer is formed by the polymerization of:(a) in the range of about 6 mole percent to about 25 mole percent of the ampholytic ion pair monomer, and (b) in the range of about 75 mole percent to about 94 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.03 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 25. The polymer of claim 6 wherein the comonomer is a alkali salt of acrylic acid.
 26. A polymer formed by the copolymerization of an effective amount of each of the following components to produce a polymer which is highly absorbent to aqueous electrolyte solutions:(a) an ampholytic ion pair monomer comprising(i) the ammonium cation 2-methacryloyloxyethyldiethylammonium and (ii) a sulfonate anion selected from the group consisting of 2-acrylamido-2-methylpropane sulfonate, 2-methacryloyloxyethane sulfonate, vinyl sulfonate, styrene sulfonate, and combinations of two or more thereof; (b) a comonomer selected from the group consisting of acrylic acid, methacrylic acid, alkali salt of acrylic acid and alkali salts of methacrylic acid and; (c) at least one crosslinking agent which has at least two polymerizable olefinic functionalities wherein each of the olefinic functionalities is suitable for crosslinking; wherein the polymer is formed by the polymerization of in the range of about 3 mole percent to about 6 mole percent of the ampholytic ion pair monomer, and in the range of about 94 mole percent to about 97 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 percent; and in the range of about 0.01 mole of the crosslinking agent to about 0.3 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 27. The polymer of claim 26 wherein the polymer is formed by the polymerization of:(a) in the range of about 3 mole percent to about 6 mole percent of the ampholytic ion pair monomer, and (b) in the range of about 94 mole percent to about 97 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.01 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 28. The polymer of claim 26 wherein the sulfonate anion is 2-acrylamido-2-methylpropane sulfonate.
 29. The polymer of claim 28 wherein the polymer is formed by the polymerization of:(a) in the range of about 3 mole percent to about 6 mole percent of the ampholytic ion pair monomer, and (b) in the range of about 94 mole percent to about 97 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.01 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 30. The polymer of claim 29 wherein the polymer is formed by the polymerization of:(a) about 3 mole percent of the ampholytic ion pair monomer, and (b) about 97 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.03 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 31. The polymer of claim 26 wherein the sulfonate anion is 2-methacryloyloxyethane sulfonate.
 32. The polymer of claim 31 wherein the polymer is formed by the polymerization of:(a) in the range of about 3 mole percent to about 6 mole precent of the ampholytic ion pair monomer, and (b) in the range of about 94 mole percent to about 97 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.01 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 33. The polymer of claim 32 wherein the polymer is formed by the polymerization of:(a) about 3 mole percent of the ampholytic ion pair monomer, and (b) about 97 mole percent of the comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (c) in the range of about 0.03 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 34. The polymer of claim 6 wherein the comonomer is a combination of acrylamide and alkali salt of acrylic acid.
 35. A polymer formed by the copolymerization of an effective amount of each of the following components to produce a polymer which is highly absorbent to aqueous electrolyte solutions:(a) an ampholytic ion pair comprising(i) the ammonium cation 2-methacryloyloxyethydiethylammonium and ii) a sulfonate anion selected from the group consisting of 2-acrylamido-2-methylpropane sulfonate, 2-methacryloyloxyethane sulfonate, vinyl sulfonate, styrene sulfonate, and combinations of two or more thereof; (b) a comonomer which is a combination of acrylamide and an alkali salt of acrylic acid and; (c) at least one crosslinking agent which has at least two polymerizable olefinic functionalities wherein each of the olefinic functionalities is suitable for crosslinking; wherein the polymer is formed by the polymerization of in the range of about 1 mole percent to about 55 mole percent of the ampholytic ion pair monomer, in the range of about 10 mole percent to about 55 mole percent of the acrylamide comonomer, and in the range of about 32 mole percent to about 89 mole percent of the alkali salt of acrylic acid comonomer, wherein the total amount of the ampholytic ion pair monomer and comonomer equals 100 mole percent; and in the range of about 0.01 mole of the crosslinking agent to about 0.3 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 36. The polymer of claim 35 wherein the polymer is formed by the polymerization of:(a) in the range of about 3 mole percent to about 50 mole percent of the ampholytic ion pair monomer, (b) in the range of about 13 mole percent to about 50 mole percent of the acrylamide comonomer, and (c) in the range of about 37 mole percent to about 84 mole percent of the alkali salt of acrylic acid comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (d) in the range of about 0.03 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 37. The polymer of claim 35 wherein the sulfonate anion is 2-acrylamido-2-methylpropane sulfonate.
 38. The polymer of claim 37 wherein the polymer is formed by the polymerization of:(a) in the range of about 3 mole percent to about 15 mole percent of the ampholytic ion pair monomer, (b) in the range of about 15 mole percent to about 30 mole percent of the acrylamide comonomer, and (c) in the range of about 55 mole percent to about 82 mole percent of the alkali salt of acrylic acid comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (d) in the range of about 0.01 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 39. The polymer of claim 38 wherein the polymer is formed by the polymerization of:(a) in the range of about 3 mole percent to about 10 mole percent of the ampholytic ion pair monomer, (b) in the range of about 20 mole percent to about 25 mole percent of the acrylamide comonomer, and (c) in the range of about 70 mole percent to about 77 mole percent of the alkali salt of acrylic acid comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (d) in the range of about 0.03 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 40. The polymer of claim 35 wherein the sulfonate anion is 2-methacryloyloxyethane sulfonate.
 41. The polymer of claim 40 wherein the polymer is formed by the polymerization of:(a) in the range of about 1 mole percent to about 55 mole percent of the ampholytic ion pair monomer, (b) in the range of about 10 mole percent to about 55 mole percent of the acrylamide comonomer, and (c) in the range of about 32 mole percent to about 89 mole percent of the alkali salt of acrylic acid comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (d) in the range of about 0.01 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 42. The polymer of claim 41 wherein the polymer is formed by the polymerization of:(a) in the range of about 3 mole percent to about 50 mole percent of the ampholytic ion pair monomer, (b) in the range of about 13 mole percent to about 50 mole percent of the acrylamide comonomer, and (c) in the range of about 37 mole percent to about 84 mole percent of the alkali salt of acrylic acid comonomer, wherein the total amount of the ampholytic ion pair monomer and the comonomer equals 100 mole percent; and (d) in the range of about 0.03 mole of the crosslinking agent to about 0.2 mole of the crosslinking agent per 100 mole of the ampholytic ion pair monomer and the comonomer.
 43. A paper towel containing therein a polymer formed by the copolymerization of an effective amount of each of the following components to produce a polymer which will absorb at least 70 grams of synthetic urine per gram of polymer:(a) an ampholytic ion pair monomer comprising(i) the ammonium cation 2-methacryloyloxyethyldiethylammonium and (ii) a sulfonate anion selected from the group consisting of 2-acrylamido-2-methylpropane sulfonate, 2-methacryloyloxyethane sulfonate, vinyl sulfonate, styrene sulfonate, and combinations of two or more thereof; (b) at least one comonomer selected from the group consisting of acrylamide, methacrylamide, acrylonitrile, acrylic acid, methacrylic acid, alkali salts of acrylic acid, alkali salts of methacrylic acid, N-vinyl-2-pyrrolidone and combinations of two or more thereof; and (c) at least one crosslinking agent which has at least two polymerizable olefinic functionalities wherein each of the olefinic functionalities is suitable for crosslinking.
 44. A disposable diaper containing therein a polymer formed by the copolymerization of an effective amount of each of the following components to produce polymer which will absorb at least 70 grams of synthetic urine per gram of polymer:(a) an ampholytic ion pair monomer comprising(i) the ammonium cation 2-methacryloyloxyethyldiethylammonium and (ii) a sulfonate anion selected from the group consisting of 2-acrylamido-2-methylpropane sulfonate, 2-methacryloyloxyethane sulfonate, vinyl sulfonate, styrene sulfonate and combinations of two or more thereof; (b) at least one comonomer selected from the group consisting of acrylamide, methacrylamide, acrylonitrile, acrylic acid methacrylic acid, alkali salts of acrylic acid, alkali salts of methacrylic acid, N-vinyl-2-pyrrolidone and combinations of two or more thereof; and (c) at least one crosslinking agent which has at least two polymerizable olefinic functionalities wherein each of the olefinic functionalities is suitable for crosslinking. 